TAPES
Bidirectional fabrics made with flat wide tapes impregnated with thermoplastic polymers. Considered also thermoplasticprepregs, because already incorporate the fiber-matrix needed for being directly consolidated. These fabrics provide anexcellent strength-to-weight ratio, greater impregnation and a smooth surface finish appearance. Blackfabric offers a widerange of spread tow fabrics with carbon, glass, and natural fiber tapes, combined with different matrices such as PA6,PA11, BIOPA, PP, PC, among others. Contact us to customize your fabric.
| CODE | REFERENCE | COMPOSITION | FABRIC CONSTRUCTION | WEIGHT | MATRIX CONTENT BY WEIGHT | DATA SHEET |
|---|---|---|---|---|---|---|
| B23-002 | TAP-CF/BIOPA-16MM-PL-300 | CF-BIOPA | PLAIN | 300 | 50% |  |
| B23-009 | TAP-CF/PA11-12MM-PL-367 | CF/PA11 | PLAIN | 367 | 37% | |
| B23-013 | TAP-CF/PP-12MM-PL-370 | CF/PP | PLAIN | 370 | 36% | |
| B23-015 | TAP-CF/PA6-12MM-PL-380 | CF/PA6 | PLAIN | 380 | 40% | |
| B23-006 | TAP-CF-/PA6-12MM-PL-450 | CF/PA6 | PLAIN | 450 | 40% | |
| B23-016 | TAP-CF-PEEK-10MM-PL-450 | CF/PEEK | PLAIN | 450 | 35% | |
| B23-001 | TAP-CF/PPA-12MM-PL-450 | CF/PPA | PLAIN | 450 | 40% | |
| B23-008 | TAP-CF/PC-12MM-PL-460 | CF/PC | PLAIN | 460 | 40% | |
| B23-004 | TAP-GF/BIOPA-16MM-PL-570 | GF/BIOPA | PLAIN | 570 | 50% | |
| B23-018 | TAP-GF/PA12-12MM-PL-620 | GF/PA12 | PLAIN | 620 | 55% | |
| B23-019 | TAP-GF/PET-12MM-PL-830 | GF/PET | PLAIN | 830 | 30% | |
| B23-017 | TAP-GF-PP-20MM-PL-840 | GF/PP | PLAIN | 840 | 50% | |
| B23-010 | TAP-DYNEEMA/PE-12MM-PL-575 | DYNEEMA/PE | PLAIN | 575 | 58% | |
- *Roll width from 100cm up to 200cm.
- *Roll length from 50 m up to 100 m.
CODE
COMPOSITION
WEIGHT
+INFO
- *Roll width from 100 cm up to 200 cm.
- *Roll length from 50 m up to 100 m.